                                 Quantification Report                              
      /export/home/kratos/data/Y05/MM-SiOx.dset              Fri Feb 19 13:46:49 2010

                                                                                      
      State #0 : Angle     0.00 degrees                                               
                                                                                      
      Peak              Position   FWHM    Raw Area   RSF    Atomic   Atomic   Mass   
                        BE (eV)    (eV)     (CPS)             Mass    Conc %  Conc %  
                                                                                      
      O 1s               532.200   1.866    15413.5  0.736   15.999   46.94   38.51   
      C 1s               285.000   2.076     2569.6  0.318   12.011   18.11   11.15   
      Si 2p               99.000   1.375     5786.0  0.371   28.086   34.95   50.34   
                                                                                      
      State #0 : Angle    20.00 degrees                                               
                                                                                      
      Peak              Position   FWHM    Raw Area   RSF    Atomic   Atomic   Mass   
                        BE (eV)    (eV)     (CPS)             Mass    Conc %  Conc %  
                                                                                      
      O 1s               533.800   1.885    17405.0  0.736   15.999   50.68   42.39   
      C 1s               286.600   2.013     2614.6  0.318   12.011   17.62   11.06   
      Si 2p              100.700   1.385     5487.8  0.371   28.086   31.70   46.55   
                                                                                      
      State #0 : Angle    30.00 degrees                                               
                                                                                      
      Peak              Position   FWHM    Raw Area   RSF    Atomic   Atomic   Mass   
                        BE (eV)    (eV)     (CPS)             Mass    Conc %  Conc %  
                                                                                      
      O 1s               533.800   1.877    18832.3  0.736   15.999   50.72   42.79   
      C 1s               286.300   1.898     2988.3  0.318   12.011   18.63   11.80   
      Si 2p              100.500   1.411     5738.9  0.371   28.086   30.66   45.41   
                                                                                      
      State #0 : Angle    40.00 degrees                                               
                                                                                      
      Peak              Position   FWHM    Raw Area   RSF    Atomic   Atomic   Mass   
                        BE (eV)    (eV)     (CPS)             Mass    Conc %  Conc %  
                                                                                      
      O 1s               534.000   1.849    18983.8  0.736   15.999   50.63   43.97   
      C 1s               286.500   1.978     3570.6  0.318   12.011   22.04   14.37   
      Si 2p              100.600   1.376     5164.4  0.371   28.086   27.33   41.66   
                                                                                      
      State #0 : Angle    60.00 degrees                                               
                                                                                      
      Peak              Position   FWHM    Raw Area   RSF    Atomic   Atomic   Mass   
                        BE (eV)    (eV)     (CPS)             Mass    Conc %  Conc %  
                                                                                      
      O 1s               534.000   1.821     5766.1  0.736   15.999   44.94   40.50   
      C 1s               286.500   1.757     1689.9  0.318   12.011   30.48   20.62   
      Si 2p              104.700   1.794     1589.0  0.371   28.086   24.57   38.87   
                                                                                      